Product Information
Product description
Operational sector:
Mipa P 20 is a laminating resin, which will get hard fast
immediately after the addition of the benzoyl-peroxid hardener.
When using glass fabric, glass cloth or glass non-woven fabric a
high performance system is obtained which permits easy and fast
repair of bigger holes at car panels or body.
Mipa P 20 is also available as complete package Mipa P 20
Repair Set
including glass fabric, brush and stirring cover.
Attributes:
Mipa P 20 and Mipa P 20 Reparatur-Set are particularly relevant for refinishers, intended for bigger holes repairment. It’s inherent properties of high build and good adhesion to iron and glass fibre reinforced plastics makes Mipa P 20 equally suitable for use as composite material (for car body and plastic parts) which confirm its versatility. Changes on car appearance are not generally allowed. Please see the relevant laws! Binder base:
Storage:
At least 1 year, if the original tins are kept closed VOC-regulation:
EC limiting value for the product (cat. B/b): 250 g/l (2007) This product contains max. 0 g/l VOC [ 0 lbs/gal] Application
Processing conditions: Degrease, derust and abrade the surface to provide an improved
key. If the substrate is an aluminium or zinc alloy it must be throughly abraded or similarly treated to remove the oxide layer and laminate immediately after that, to ensure that the key is adequate. Mix recommendations.
To achive the best possible finish it is advisable to recover the
surface either with Mipa P 90 or Mipa P 99 Multi-Star.
Processing conditions: between +5°C and +30°C.
Attention: if the material is used below the dew point, its
adhesivity would be much reduced.
Mixing ratio:
Mix thoroughly Mipa P 20 with 1 - 3% hardener Mipa Härter P. This data sheet is for information purpose only! To our knowledge the data provided complies with the latest standard and is based on years of experience in the manufacture of our products. However the data is not binding and without warranty. Please follow recommendations stated on the relevant safety data sheet and precautions stated on the product label. We reserve our right to make additions, deletions, or modifications to the information at any time without prior notification. MIPA AG · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100
Product Information
Pot life:
About 10 - 15 minutes by 20°C temperature of the environment and 2% hardener. Mipa P 20 will get hard after about 60 min. by 20°C environment
temperature. A noticeable acceleration of the hardening process is
quoted by stove drying at 50°C or by using IR lamps .
Attention: min. temperature for use + 10°C . A lower temperature
does not allow to set hard!
Sanding:
After 60 min. with P 60 - P 80 sanding paper. Safety Instructions
Use only in well ventilated rooms. Do not smoke, eat or drink during application. Keep away from children. When the ventilation is not adequate, suitable individual respiratory protection must be worn. Cleaning of Tools

Tools should be cleaned immediately after use with Mipa Universalverdünnung. When set
hard the putty cannot be removed.



This data sheet is for information purpose only! To our knowledge the data provided complies with the latest standard and is based on years of experience in the manufacture of our products. However the data is not binding and without warranty. Please follow recommendations stated on the relevant safety data sheet and precautions stated on the product label. We reserve our right to make additions, deletions, or modifications to the information at any time without prior notification. MIPA AG · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100

Source: http://mipa.de/gb/pi/lm/P20_lang.pdf

fhpr2a.fr

Si la psychiatrie est souvent considérée comme une discipline à domaine des pathologies cardiovasculaires. Difficile donc de soigner part, difficile à aborder par le non-spécialiste, elle fait pourtant l’une sans l’autre. partie intégrante de la pratique des généralistes. Enfin, certaines pathologies dites psychiatriques pourraient A cela plusieurs raisons. D’une p

Vol-15_no-4a.pdf

Polish J. of Environ. Stud. Vol. 15 No. 4A (2006), 59-61 About the Interaction of Human Serum Albumin with Nevirapine and Azidothymidine A. Kluczewska1, K. Michalik1, Z. Drzazga1, M. Kaszuba2 1University of Silesia, A. Cheákowski’ Institute of Physics, Department of Medical Physics, Uniwersytecka 4, 40-007 Katowice, Poland 2Medical University of Silesia, Department of Prosthetic

Copyright © 2010-2014 Internet pdf articles